摘 要:从腐蚀机理、水质和煤质影响、煤粉流动稳定性等方面分析了壳牌煤气化炉烧嘴罩发生漏水失效问题的原因;针对工程设计、施工管理和操作控制提出了改进措施和应对策略。
关键词:壳牌煤气化;烧嘴罩;腐蚀;磨蚀;过烧;应对措施
中图分类号:TQ545 文献标识码:A 文章编号:1004-8901(2011)05-0023-06
Failure Reason Analysis and Repartee Repartee Strategy for Burner Muffle of Shell Coal Gasifier
XU Cai-fu,YIN Wei-yu,LI Jia-wei,CAI Yong-ning
(China Wuhuan Engineering Company Ltd.,Wuhan Hubei 430223 China)
Abstract:Author has analyzed the failure reason for water leakage occurred in Shell coal gasifier muffle from aspects of corrosion mechanism,effect of water quality and coal quality,stability for now of pulverized coal and so on;and has presented the improvement measures and repartee strategy in allusion to engineering design,construction management and operational control.
Key words:Shell coal gasifieation;burner muffle;corrosion;erosion;over-burning;repartee measares
到目前为止,采用壳牌粉煤加压气化技术的煤气化装置已有15套投入运行,还有3套正在试运行。为了达到装置的长周期安全运行,壳牌公司、中石化公司、合肥通用机械研究所、业主及工程公司进行了大量研究和开发工作,提出不少改进措施,壳牌公司还相继推出了第Ⅱ代、第Ⅲ代烧嘴罩。由于这些改进的重点是材料、烧嘴罩结构以及烧嘴与烧嘴罩之间的密封结构,尽管改进后烧嘴罩能适应较大的操作弹性,但烧嘴罩的穿孔漏水现象仍然时有发生。其原因是:由于熔融的渣沿突出的烧嘴罩端部分流的结果可能导致烧嘴罩下方膜式壁局部不能形成良好的渣层保护,膜式壁水冷管直接与火焰接触,且由于热流通量过大,引起局部过烧或形成高温S和P的共晶体,产生高温腐蚀和裂纹。因此烧嘴罩失效漏水问题依然是制约煤气化装置长周期运行的关键因素之一。鉴于此,笔者拟从失效机理入手,对工程设计、制造检验、操作管理等进行综合分析,以期彻底解决烧嘴罩的失效问题。
1 烧嘴罩结构
烧嘴罩安装在气化炉反应室膜式壁处,与煤烧嘴和反....